Properties of Mg & Al alloys
Mechanical property limits for various Mg and Al alloys in die forgings
|
Alloy grade |
UTS MPa |
YTS MPa |
Elongation % |
|
AZ61A-F |
262 |
152 |
6 |
|
MA2-1-F |
265 |
- |
7 |
|
AZ31B-F |
234 |
131 |
6 |
|
MA14-T5 |
295 |
- |
7 |
|
2014-T6 |
450 |
385 |
6 |
|
2024-T6 |
427 |
345 |
5 |
|
7075-T6 |
515 |
440 |
7 |
Mechanical properties of extruded round bars and forgings from MA14 (ZK60) alloy
|
Product |
UTS (MPa) |
YTS (MPa) |
Elongation (%) |
Hardness (HB) |
Property |
|
ERB, T5 |
265 |
175 |
4 |
|
Min. guaranteed |
|
ERB, T5 |
343 |
294 |
9 |
- |
Typical |
|
Forgings, T5 |
295 |
- |
7 |
64 |
Min. guaranteed |
|
Forgings, T5 |
314 |
255 |
14 |
|
Typical |
Properties of 2024-Т6 и 7075-Т6 alloys for die forgings for wall thicknesses from 25 to 50 mm
|
Property |
2024-Т6 |
7075-Т6 |
Notes |
|
Density, g/cm3 |
2,78 |
2,81 |
Typical |
|
UTS, MPa |
427 |
510 |
Min. guaranteed |
|
YTS, MPa |
345 |
435 |
Min. guaranteed |
|
Elongation at Break, % |
5 |
7 |
Min. guaranteed |
|
Modulus Elasticity, GPa |
72,4 |
71,7 |
Typical |
|
Hardness, HB |
125 |
150 |
Typical |
|
Fatigue Strength, MPa |
124 |
159 |
Typical |
|
CTE linear, μm/m-0C |
23,2 |
23,6 |
Typical |